Adsyl 7416 XCP is an advanced polyolefin selected by customers for use as a sealing layer in coextruded film applications. This grade features a low seal initiation temperature and good optics. It does not contain slip or anti-block additives.
Adsyl 7416 XCP
Description
Availability
Africa-Middle East, Asia-Pacific, Australia and New Zealand, Europe, North America, South & Central America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 7.5 g/10 min |
| Density (23 °C, Method A) | 0.90 g/cm³ |
| Flexural Modulus | 600 MPa |
| Tensile Stress at Yield | 21 MPa |
| Tensile Strain at Yield | 14 % |
| Tensile Young's Modulus MD (50 µm, 25 mm/min) | 290 MPa |
| Tensile Young's Modulus TD (50 µm, 25 mm/min) | 320 MPa |
| Tensile Stress at Break MD (50 µm, 500 mm/min) | 40 MPa |
| Tensile Stress at Break TD (50 µm, 500 mm/min) | 42 MPa |
| Tensile Stress at Yield MD (50 µm, 500 mm/min) | 15 MPa |
| Tensile Stress at Yield TD (50 µm, 500 mm/min) | 15 MPa |
| Seal Initiation Temperature | 115 °C |
| Vicat Softening Temperature (A50) | 115 °C |
| Heat Deflection Temperature B (0.45 MPa, Unannealed) | 52 °C |
| DSC Melting Point | 133 °C |
| Haze (50 µm) | 0.5 % |
| Gloss (45°, 50 µm) | 90 |
Technical Data Sheet
Technical Data SheetProcess
BOPP, Cast Film, Double Bubble
Resin
Catalloy
Applications
Food Packaging Film, Lamination Film, Shrink Film, Stationery Film, Stretch Wrap Film